- Standard: ASTM B209, GB/T 3880, EN AW etc
- Certifications: CE, ISO, SGS etc
- Shipping methods: Express, sea freight, air cargo, land transportation, postal etc
- Sample service: we can provide samples, and the samples are free.
what is 6082 aluminum sheet?
6082 aluminum sheet heat treatment can strengthen the alloy, with good formability, weldability, machinability and corrosion resistance, while a moderate strength, after annealing can still maintain good operability, mainly for mechanical structure Including bars, sheet, tube and profile.
6082 and 6061 aluminum sheet are both Al-Mg-Si aluminum alloy which can be strengthened by aging treatment, with good extrusion and forging properties, and good anodizing properties. Since 6082 is a heat treatable alloy, strength will be reduced in the weld region. 6082 aluminum sheet and sheet are typically formed by rolling. Signi offers alloy 6082 sheet and sheet for highly stressed applications includes trusses, bridges, cranes, transport applications as well as mould
In addition, 6082 aluminum sheet also has the following characteristics:
1. Good formability, solderability and brazeability.
2. It has medium strength and good machinability.
3. Good usability and excellent interface characteristics.
4. Easy to process, good anode reaction performance and easy coating.
5. Good corrosion resistance and oxidation resistance.
Parameters of 6082 aluminum sheets
| Equivalent name | a6082, 6082a, aa6082, 6082aa, al6082, al6082a, 6082 aa, aa 6082, jis a6082p, al6082 class, aw6082 grade etc |
| Temper | Soft HO, H11, H12, H13, H14, H15, H16, H17, H18, H19, H20, H21, H22, H23, H24, H25, H26, H27, H28, H29, H30, H31, H32, H33, H34, H35, H36, H37, H38, H39, H46, H111, H112, H114, H116, H131, H321 etc T0, T2, T3, T4, T5, T6, T7, T8, T24, T32, T35, T73, T74, T83, T351, T354, T650, T651, T851 etc |
| Thickness | ( thin ) 0.3mm, 4.5mm, 5mm, 10mm, 15mm, 19mm, 20mm, 25mm ( thick ) etc |
| Size | ultra width ( 2500mm ) etc |
Chemical composition of 6082 aluminum sheets
| Si ( Silicon ) | Cu ( Copper ) | Mg ( Magnesium ) | Zn ( Zinc ) | Mn ( Manganese ) | Cr ( Chromium ) | Fe ( Iron ) | Ti ( Titanium ) | Other | Others total | Al ( Aluminum ) |
| 0.7 – 1.3 | ≤ 0.1 | 0.06 – 1.2 | ≤ 0.2 | 0.4 – 1.0 | ≤ 0.25 | ≤ 0.5 | ≤ 0.1 | ≤ 0.05 | ≤ 0.15 | remainder |
6082 T6 Aluminum Sheet typical Mechanical Properties
- Tensile strength σb (MPa): ≥205
- Conditional yield strength σ0.2 (MPa): ≥110
- Elongation δ10 (%): ≥14
Note: Longitudinal mechanical properties of profile at room temperature
Sample size: all thickness
Homogenization temperature: 555-565℃ Holding time: 3 hours, cooling rate ≥200℃/
| Material | Thickness (mm) | Tensile Strength (N/mm²) min | Yield Strength (N/mm²) min | Elongation on 50mm % (min) |
| Alloy 6082 – T6 Sheet | 0.2 – 3.0 | 295 | 255 | 8 |
| Alloy 6082 T6 Sheet | 3.0 – 6.0 | 295 | 240 | 8 |
| Alloy 6082 T6 Sheet | 6.0 – 25.00 | 295 | 240 | 8 |
O – Soft
T6 – Solution heat treated and artificially aged
T4 – Solution heat treated and naturaly aged to a substantially stable condition
T651 – Solution heat treated, stress relieved by stretching then artificially aged
T651 – Solution heat-treated, stress-relieved by controlled stretching and minor straightening is allowed after stretching to comply with standard tolerances then artificially aged.
6082 alloy aluminum sheet smelting process
1. Smelting
6082 alloy is characterized by containing Mn, Mn is a refractory metal, the melting temperature should be controlled at 740-760 ℃. Stir more than twice before sampling to ensure that the metal is completely melted, the temperature is accurate, and the composition is uniform. After stirring, take a sample in the middle of the depth of the molten aluminum and on the left and right sides of the furnace for analysis.
2. Purification and casting
After the melt is transferred to a static furnace, it is sprayed with nitrogen and a refining agent for spraying and jet refining. The refining temperature is 735-745°C for 15 minutes. After refining, it is allowed to stand for 30 minutes. Through this process degassing, slag removal, and purification of the melt.
During the casting process, there are two filtering devices between the casting mold and the furnace port. The furnace port has a foam ceramic filter sheet (30PPI) for filtering. Before casting, it is filtered with 14 mesh glass fiber wires cloth to fully filter out the oxides and slag inclusions in the melt.
The casting temperature of 6082 alloy aluminum sheet is high (compared to the normal process of 6063 aluminum sheet), the casting speed is low, and the water flow is large. The above process needs to be strictly controlled and cannot exceed the range, otherwise it will easily lead to casting failure.
Heat treatment process of 6082 aluminum sheet
Melting 6082 alloy is characterized by containing Mn, which is a refractory metal, and the melting temperature should be controlled at 740-760℃. Stir evenly for more than two times before sampling to ensure that the metal is completely melted, the temperature is accurate, and the composition is uniform. After stirring, take a sample in the middle of the molten aluminum depth and on the left and right sides of the furnace for analysis, and the converter can be converted after the analysis is qualified.
Purification and casting After the melt is transferred to the static furnace, it is sprayed with nitrogen and refining agent and refined by air jet. The refining temperature is 735-745°C for 15 minutes. After the refining, it is allowed to stand for 30 minutes. Through this process, degassing, slag removal, and melt purification. There are two filtering devices between the mold and the furnace mouth during casting. The furnace mouth is filtered by a foam ceramic filter sheet (30PPI). Before casting, it is filtered with a 14-mesh glass fiber cloth to fully filter out the oxides and slag inclusions in the melt.
The casting temperature of 6082 alloy aluminum sheet is relatively high (compared with the normal process of 6063 aluminum sheet), the casting speed is relatively low, and the water flow is relatively large. The above process needs to be strictly controlled and cannot exceed the range, otherwise it will easily lead to casting failure.
Applications for 6082 Aluminum Sheet
Aviation fixtures, trucks, towers, ships, tubelines and other construction applications where strength, weldability and corrosion resistance are required. Such as: aircraft parts, camera lenses, couplers, marine accessories and hardware, electronic accessories and connectors, decorative or various hardware, hinge heads, magnetic heads, brake pistons, hydraulic pistons, electrical accessories, car fuel tank, traffic vehicles, valves and valve parts etc
With the rapid development of the shipbuilding industry at home and abroad, reducing the weight of the hull, increasing the speed of the ship, and seeking to replace aluminum alloy materials with steel parts, it has become an important issue facing the aluminum processing industry and the shipbuilding industry. 6082 aluminum sheet’s high quality and light weight make it an ideal material for high-speed ship components.
- Good formability, weldability, machinability and corrosion resistance;
- 6082 Aluminum Sheet with moderate strength, after the annealing can still maintain a good operability;
- Good anode reaction performance, the most commonly used anode reaction methods include the removal of impurities and dyeing， coating and so on;
- 6082 aluminum sheet -0 and T4 state for bending and forming the occasion;
Popular applications
Mould machining etc
Aluminum sheet manufacturers near me
Henan Signi Aluminum Co., Ltd. is the leader of many aluminum manufactures and suppliers in China. We strictly control the quality and focus on customers. We hope to have in-depth cooperation with you and provide you with high quality aluminum material prodsucts custom OEM services. If you want to get the newest and best prices by per kg ( kilogram ) or per ton standard weight, please contact us.
Aluminum sheet sheet standard export packing
- The aluminum sheet is paperclip or laminated to ensure that the surface of the aluminum sheet is intact and free of scratches;
- Plastic film ( HDPE, PVC, PE or PET etc ) protection or hard kraft paper wrapping is used to prevent moisture and rain to ensure that the aluminum sheet is clean and free of dirt during transportation (each package has a moisture-proof desiccant to ensure the quality of our prodsucts in East China and South China, where there is more rain);
- Installed with wooden brackets and reinforced with steel straps to avoid collision during transportation and to ensure the geometry of the aluminum sheet remains unchanged;
- For export prodsucts, we use wooden boxes and pallets with fumigation mark for packaging;
- We can also pack according to other packaging requirements of customers;