Prodsuct Introdsuction
1.6082 the heat treatment can enhance alloy, with good formability and weldability, processability and,
2. with moderate intensity at the same time, can still maintain a good operational after annealing, mainly for the mechanical structure, such as bars, sheet, tube and profile.
3. This kind of alloy has and mechanical properties of 6061 alloy is similar but not identical, its - T6 state has high mechanical properties.
4. Alloy 6082 is a common alloy prodsuct in Europe and has high application in the United States. It is suitable for processing raw materials, seamless aluminum tubes, structural profiles and customized profiles.
5.6082 alloy usually has a good processing properties and good anodic reaction performance.The most commonly used anodic methods include removal of impurities, removal of impurities and staining, coating, etc.alloy
Chemical Composition
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others | Al |
| 0.25 | 0.40 | 0.10 | 0.10 | 2.2-2.8 | 0.15-0.35 | 0.10 | / | 0.15 | Balance |
Mechanical Property
| Material Grade | Temper | Diameter(mm) | Tensile Strength | Yield Strength |
| 5052 | H112 | 50mm | ≥170Mpa | ≥70Mpa |
| 5052 | O | 50mm | 170-230 | ≥70Mpa |
Prodsuct Application
1. All kinds of industrial structural parts with certain strength, weldability and corrosion resistance are required, such as tubes, rodss and profiles for making trucks, tower buildings, ships, trams, railway vehicles, furniture, etc.
2.6082 alloy usually has a good processing properties and good anodic reaction performance;Widely used in mechanical parts, forgings, commercial vehicles, railway structural parts, shipbuilding, etc.